MT-13™ Epoxy glue /142gr

Smooth-On MT-13™ ist ein Hochleistungs-Epoxidharz für Anwendungen, die maximale Haltekraft und Wasserbeständigkeit erfordern. MT-13™ ist ein Zweikomponenten-Epoxy-Klebzement, der zu gleichen Volumenteilen gemischt wird (100A/123B nach Gewicht). Die Topfzeit beträgt 35 Minuten und die Handhabungsfestigkeit entwickelt sich in 16 Stunden bei 23 °C. MT-13™ haftet extrem gut sowohl auf porösen als auch auf nicht porösen Oberflächen. MT-13™ wird in der Bootsindustrie häufig für die Montage und allgemeine Reparatur verwendet. MT-13™ behält seine Haltekraft auch unter extrem kalten Bedingungen.

Instructions

Safety - Use in a properly ventilated area (“room size” ventilation). Wear safety glasses, long sleeves and rubber gloves to minimize contamination risk.

Store and use material at room temperature 23°C. This product has a limited shelf life and should be used as soon as possible.

A clean, dry surface is a necessary prerequisite for adhesive bonding. Adhesives will stick to either the surface of which a bond is desired or to that film of extraneous material directly on that surface. Rarely can a structural adhesive penetrate through surface contaminants to provide an optimum bond on an unclean surface.

Porous materials are simple to bond, provided they are dry. The surface should be sanded till clean and free from dust. Nonporous surfaces, such as found on metal and plastic materials, should be degreased, dried and roughened by sanding, sandblasting or chemical etching. The etched or sandblasted surfaces should be covered within a few hours of treatment to prevent contamination.

Epoxy adhesives do not perform well on metals such as nickel, chromium, tin or zinc nor on soft thermoplastics like polyethylene. Refer to the Preparation of Surfaces for Adhesive Bonding technical bulletin.

Because no two applications are quite the same, a small test application to determine suitability for your project is recommended if performance of this material is in question.

MIXING AND APPLYING...

Measure equal amounts of Parts A and B (or 100A:123B by weight) and mix thoroughly for 3 minutes to a uniform color (no streaks). Apply to prepared surface at a thickness of 0.08cm - 0.16cm. Fit other surface over epoxy and apply even pressure using clamps or weights until material cures.

CURING...
MT-13™ will cure and reach handling strength in 16 hours at room temp. 23°C Applying uniform mild heat will cure epoxy faster 65°C for 4 hours. Let cool to room temperature before moving bonded substrates.